This site makes use of cookies necessary for the operation and useful for the purposes described in the cookie policy. If you want to learn more, see the cookie policy. By closing this banner, scrolling this page, clicking on a link or continuing navigation in any other way, you consent to the use of cookies.
The changes in magnesia-spinel bricks from preheater cement kilns using alternative fuels were studied. An analysis of the wear mechanism of bricks was made based on the evolution of apparent porosity, the variation of their chemical compositions and investigation of their microstructure in relation to the internal temperature gradient. The investigation shows that persistence of a coating on the basic refractory lining of the sintering zone does not only effectively protect it against the direct influence of the temperature and corrosive reactions with components of the sintered Portland clinker, but also alleviates the influence of volatile components of the kiln atmosphere on the refractories. Dramatic variations of the volatile components in the kiln atmosphere with simultaneous change of manufactured cement clinker type may lead to coating disappearance and direct exposure of the lining to the influence of the high temperature and aggressive corrosion by components of the sintered Portland clinker and the kiln atmosphere. Excess of chloride and SO3 leads to MgO corrosion. Substantial excess of R2O (R = K, Na) leads to intensive corrosion of main components in the colder part of bricks and weakening of the bricks texture.
The effects of nano calcium carbonate on the properties of corundum-based castables were investigated. White fused alumina, ultra-fine alumina, nano calcium carbonate, calcium aluminate cement and hydratable alumina were used as raw materials. The results show that the phase compositions and phase changes of the mixture with nano calcium carbonate addition treated above 900 °C are the same as those of the mixture with calcium aluminate cement. The hot and cold modulus of rupture of the castables with nano calcium carbonate above 800 °C is improved by the bonding of in-situ reaction products and is higher than that of the castables with calcium aluminate cement, especially at 800 °C. The thermal shock resistance of the castable is enhanced by adding nano calcium carbonate or calcium aluminate cement. There is no evident difference between the effects of the two additives. The slag corrosion resistance of the castable is deteriorated by adding a small amount of nano calcium carbonate or calcium aluminate cement compared to the castable without CaO, but it is improved with higher CaO content. The castable with nano calcium carbonate is better in slag resistance than the one with calcium aluminate cement, in spite of their similar CaO content.
Chemical resistance and high elastic modulus are currently two of the most important characteristics of ceramic rollers, the former allowing for longer roller lifetime and the latter making it possible to handle heavier loads and large format tiles without adverse consequences in terms of tile planarity,
Spinel pigments of sea-green, light blue and moderate blue color were prepared from exhausted catalysts containing γ – Al2O3 as main phase, MoO3 as secondary phase and CoO, NiO or both as accessory phases, after slight correction of their composition. The color indices of the pigments were determined using a computer program, as well as their color according to the CIE standard.
The possible use of silica sludge for the production of lightweight aggregates is reported. The results show that the investigated silica sludge can serve as a raw material for the production of lightweight aggregates. The following parameters have been found to significantly influence the process: (i) the mineral composition of the basic materials, (ii) foaming agents, and (iii) the temperature range of firing/foaming. The silica sludge contains about 70 wt.% of quartz, about 5-7 wt.% of feldspar, and the rest is clay. The grain size of silica sludge is below 100 mm, and 58 wt.% is below 20 mm. In order to improve the properties of the obtained aggregate some additional waste materials (paper mud, waste glass) were added to the silica sludge. Depending on the pore forming/foaming agents and firing regime lightweight aggregate with densities between 0.6 and 1.8 g/cm3 were obtained and tested for their suitability as a construction aggregate.
The aim of this work is to evaluate the effects of incorporating river silt originated from washing silica sands extracted in “Ria de Aveiro” as a raw material in the manufacturing process of traditional ceramic building products such as bricks and tiles and on their final properties. The solid river silt waste was physico-chemically characterized for particle size distribution, morphology and XRF. The thermal behaviour was investigated by DTA and TGA analysis, and the mineralogical phases were identified by XRD. Testing bars made of several compositions incorporating amounts in the range of 0 to 10-wt% of river silt and of an industrial standard paste were produced in a pilot-plant extruder, and fired at different temperatures in the range of 950-1100 ºC. The characterisation results of sintered specimens (water absorption, linear shrinkage and mechanical bending strength) have shown that products with final properties similar to those obtained from the standard industrial body could be achieved from a composition incorporating up to 5 wt% of river silt waste.
A solid oxide fuel cell (SOFC) electrochemically converts chemical energy of a fuel into electricity at temperatures from about 650 to 1000 °C. SOFCs offer certain advantages over lower temperature fuel cells, notably ability to use CO as a fuel rather than being poisoned by it, and high grade exhaust heat for combined heat and power, or combined cycle gas turbine applications. This paper reviews the operating principle, materials for different cell and stack components, cell designs, and applications of SOFCs. Among different designs of solid oxide fuel cells (SOFCs), the electrical resistance of tubular SOFCs is high, and areal power density (W/cm2) and volumetric power density (W/cm3) low. Planar SOFCs, in contrast, are capable of achieving very high power densities.
Address
Links
Information